倍韧/BESTPERNE® ZF55B
热塑性弹性体Thermoplastic Elastomer
产品说明Product description
一款高性能吸震材料，具有特别舒适的手感。
high performance shock absorption material,with a special and comfortable feel.
关键特性Key characteristic
1.表面微亮，手感细腻柔软爽滑. A little bright on the surface，exquisite，smooth and soft touch feeling.
2.阻尼效果优异. Damping effect is good.
功能Function
Main application
手机保护套Phone protective cover
密封垫片Sealing gasket
电子器件粘胶配件Electronic plastic accessories
加工方法Processing method
注塑、挤出成型Injection and extrusion molding
Environmental certification
少许树脂味A little resin smell
外型Appearance
圆球形小颗粒Cylindrical particle，about 3mm×1.5mm
储藏期Storage period
常温下通风干燥，24个月Ventilated dry at normal temperature，about 24 months
包装方式Packaging method
25公斤/袋 25kg/bag
物理性能Physical properties
成型条件Molding condition
比重Specific gravity
干燥温度Drying temp 60 ℃
硬度Hardness
ASTM D2240
干燥时间Drying time 2h
拉伸强度Tensile strength
射嘴温度Nozzle temp 200℃
断裂延伸Elongation at break
螺筒一段温度Screw 1 temp 190℃
撕裂强度Tearing strength
螺筒二段温度Screw 2 temp 180℃
熔融指数Melt index
ASTM D1238
螺筒三段温度Screw 3 temp 170℃
压缩永久变形（高温）Compression set (high temperature)
70℃/24h，压缩量为25%
压缩永久变形（常温）Compression set (normal temperature)
23℃/72h，压缩量为25%
脆化温度Embrittlement temperature
塑料增韧的主要方法是以弹性体(TPE)为分散相，塑料为基体共混增韧，能大幅提高塑料的冲击强度。弹性体增韧塑料主要要满足三个条件：
1.弹性体与树脂形成两相结构，但也要有适度的相容性以保证两相之间有良好的粘接力;
2.弹性体添加量要达到一定的份数;
3.弹性体的分子链柔性要较低，也就是说需要较低的Tg，尤其是低温增韧时弹性体的Tg越低，低温韧性越好。
由于纯弹性体是非极性材料，而塑料(如PA、PBT)是极性材料，二者不相容，纯弹性体不能有效增韧塑料，故而需要通过接枝改性使POE形成POE接枝物，接枝的官能团能够与基材端基反应从而提供一定的相容性，使两相具有很好的粘接性，从而能够使基材树脂大幅提高冲击强度。如CMG5805-L(POE-g-MAH)的MAH可与尼龙的端胺基反应，可以有效增韧PA，当5805-L添加一定份数后，形成了超韧材料.
TPR新材料 厂家/供应 tpe原料透明 注塑级 高回弹 TPR弹性体EN3013N-1
TPE价格/ TPR/厂家供应tpe原料 食品级 美国FDA认证EN3013N
TPE/-506 TPE原料 食品级 符合FDA与LFGB标准 婴儿用品EN2582AP
通用级TPO/tpo防水卷材 自粘防水材料 脚轮轮子 厨房厨具EN2562AP
TPE/护目镜/防飞沫/食品级弹性体/TPR/高透明/弹性好/厂家直销 EN2549B
tpe颗粒 厂家 江苏供应商/玩具 5A TPR材料/ 当日出货EN2062AP
网站建设：中企动力 惠州
销售热线：400-800-0302 手机：13602342196 电话：0752-6768128 传真：0752-6768088
地址：广东省惠州市博罗县石湾镇黄西工业园径二路 邮箱：sales@tpe-sp.com 网址：www.tpe-sp.com